Model No.: PR-POM-1
POM is a kind of engineering plastic with good mechanical properties. POM together with UHMW PE, Nylon, PTFE are known as four most abrasion resistant plastics. It has almost the same rigidity as metal, so it's an ideal replacement material of copper, cast zinc, steel, aluminum and other metal materials. We are able to produce POM products without bubbles or cracks.
-High surface hardness
-Good wear resistance
-Nice self-lubricating properties
-Good dimensional stability
-Low water absorption
-Work under the temperature of -40-100 centidegrees
POM bearings own excellent stability and good wear resistance in various kinds of moist environments.
POM has high stiffness and rigidity, good self-lubricating properties. So it has taken the place of metal gears in many applications. (Prior materials: Bronze, Stainless Steel)
Guide rollers machined from POM rod operate smoothly and reliably in lift gate systems used to load cargo onto truck beds. (Prior materials: Cast Iron, Cast Aluminium)
With excellent fatigue and impact resistance, POM is a suitable material of continuously loaded structural keel for prosthetic device. (Prior materials: Nylon, PU)
Low coefficient friction, wear resistant, self-lubricating, no need for lubricating oil.
Technical Data Sheet
|Water absorption 24hrs||ISO 62||%||< 0.3|
|Heat deflection temperature - HDT/A||ISO 75A||ºC||110|
|Min. service temperature||ºC||-40|
|Max. service temperature||ºC||100|
|Thermal conductivity at 23 ºC||DIN 11359||W/(K*m)||0.31|
|Coefficient of linear thermal expansion||ISO 11359||10-4*K-1||1.2|
|Flammability Rating(6mm thickness)||UL 94||-||HB|
|III.Mechanical Properties at 23ºC|
|Tensile strength at yield||ISO 527-2||MPa||63|
|Tensile strength at break||ISO 527-2||Mpa||-|
|Elongation at break||ISO 527-2||%||31|
|Modulus of elasticity after tensile test||ISO 527-2||MPa||2,700|
|Modulus of elasticity after flexural test||ISO 178||MPa||-|
|Hardness - Shore D||DIN 53505||83|
|Charpy impact strength||ISO 179||kJ/m2||N. B.|
|Friction coefficient||DIN 53375||0.35|
|IV.Electrical Properties at 23ºC|
|Dielectric constant at 1 MHz||IEC 60250||106Hz||3.8|
|Dielectric loss factor at 1 MHz||IEC 60250||106Hz||0.005|
|Volume resistively||IEC 60093||Ohm (Ω) * cm||>1013|
|Surface resisively||IEC 60093||Ohm (Ω)||>1013|
|Dielectric strength||IEC 60243-1||kV/mm||40|
|NOTE: 1 g/cm3 = 1,000 kg/m3, 1 Mpa = 1 N/mm2, 1kV/mm = 1 MV/m|
|Property data contained herein are typical values of resin for your reference and comparison purposes only. PRIOR will not provide any legally binding guarantee of certain properties, or any suitability.|
1, three anti-static floor, the use of high-strength, fireproof, waterproof material for the substrate, dual anti-static veneer. Excellent waterproof and moisture resistance, strong bearing capacity, suitable for large and medium-sized engine room. 2, all steel anti-static raised floor, high-quality steel plate after...
1. Firstly, the total area (or number of blocks) of the anti-static floor required for computer room construction and the number of various accessories (standard ratio 1:3.5, 1:5.5) need to be accurately established, and a margin is left to avoid wastage. Or shortage. 2. To fully understand the variety and quality of...
For small and medium-sized computer rooms, in order to prevent the adverse effects of static electricity on the equipment in the equipment room, you must consider installing and using anti-static raised floor. Because it offers the following advantages: 1. It simplifies installation and provides greater flexibility for...
Model NO.: EGS-SA-023 Condition: New Type: Chair Usage: Electronic Component Maintenance Room Rotary: Rotary Stool Surface: Stainless Steel Stamping Molding, Gl Bottom: Carbon Steel of The Lacquer That Bake Lift Distance: 140mm Is Customized: Yes Transport Package: 1 PCS/Box Origin: Shenzhen China Certification: CCC, CE...
Product Categories : POM Sheet&Rod